Products
H-175K
semi-rigid
abrasion
chemical
High withstand to abrasion and cut-through；Excellent chemical and solvent resistance
留言
- Basic Information
- Technical Parameter
- Ordering Data
-
Features:
Semi-rigid
High withstand to abrasion and cut-through
Excellent chemical and solvent resistance
Highly Flame retardant
Materials PVDF Colors BK, CL Operating Temperature -55 to 175 ℃ Shrink Ratio 2:1 Product Size 1.2-25.4 mm Markets:
Automotive, Industrial
Standards:
Design for major Automotive OEM sealing specifications
Typical Applications:
Strain relief and insulation of high temperature wires
Suitable for applications for high chemical and abrasion resistance is required
All application where excellent electrical insulation is required
-
Technical Data：
Test Items
Test Method
Test Requirements
Tensile strength
ASTM D 2671
34.5MPa min.
Ultimate elongation
ASTM D 2671
150% min.
Ultimate elongation after aging at
250 ℃ for 168 hrs
UL 224
50% min.
Heat shock at 300 ℃ for 4 hrs
ASTM D 2671
No dropping & cracking
Dielectric strength
ASTM D 2671
25kV/mm min.
Volume resistivity
ASTM D 2671
1013Ω.cm min.
Cold bend at -40 ℃ for 4 hrs
ASTM D 2671
No cracking
Flammability
UL 224, VW-1
Pass
-
Product Dimensions：
Size
As supplied
After recovered
D*(Min.)
d*(Max.)
w*(Min.)
Inch
mm
mm
mm
3/64"
1.2
0.6
0.20
1/16"
1.6
0.8
0.20
3/32"
2.4
1.2
0.23
1/8"
3.2
1.6
0.23
3/16"
4.8
2.4
0.23
1/4"
6.4
3.2
0.23
3/8"
9.5
4.8
0.28
1/2"
12.7
6.4
0.32
3/4"
19.1
9.5
0.36
1"
25.4
12.7
0.41
D* = Inner diameter as supplied
d* = Inner diameter after fully recovered
w* = Wall thickness after fully recovered