Features:
High shrink ratio,Crystal clear, semi-rigid, with integral solderless splice connectors, clarity for visual confirmation of seal
Seals & protects against water, corrosive compounds, moisture & contaminants
Tough, durable heat shrink tubing resists abrasion, crimp tool damage & splitting
Meets & conforms to OEM wiring specifications for installation & repairs
Materials Polyolefin Colors BK, CL Operating Temperature -40 to 125 ℃ Shrink Ratio > 3:1 Product Size 12.0-40.0 mm Markets:
Automotive, Industrial
Standards:
Design for major Automotive OEM sealing specifications
Typical Applications:
Flat battery terminals and eyelet terminals
Aluminum copper joint connections
-
Technical Data：
Test Items
Test Method
Test Requirements
Tensile strength
ASTM D 2671
10.4MPa min.
Ultimateelongation
ASTM D 2671
250% min.
Thermal aging at 158 °C for 168 hrs
Tensile strength
Ultimateelongation
ASTM D 2671
7.3MPa min.
100% min.
Heat shock at 225°C for 4 hrs
ASTM D 2671
No dropping & cracking of outer jacket
Cold bend test at -40 °C for 1 hrs
ASTM D 2671
No cracking
Combustion behaviour
FMVSS 302
100mm/min max.
Corrosive action
ASTM D 2671
non-corrosive
Compatibility with copper
ASTM D 2671
non-corrosive
Water absorption
ISO 62
0.5%max.
Dielectric strength
ASTM D 2671
15kV/mmmin.
Volume resistivity
ASTM D 2671
1012Ω. cm min.
-
Product Dimensions：
Part Number
As supplied
After recovered
D*(Min.)
d*(Max.)
w*(Min.)
mm
mm
mm
BHT 1
12.0
3.0
2.0
BHT 2
16.0
4.0
2.5
BHT 3
24.0
6.0
2.8
BHT 4
32.0
8.0
3.1
BHT 5
40.0
10.0
3.1
D* = Inner diameter as supplied
d* = Inner diameter after fully recovered
w* = Wall thickness after fully recovered