Features:
High shrink ratio to fit varying splice configuration
Seal and protects against water, moisture and chemicals
Adhesive bonds readily to PVC, XLPE and PP - EPDM cable jackets
Quick installation due to rapid shrinkage
Materials XLPO+PA Colors BK, CL Operating Temperature -40 to 125 ℃ Shrink Ratio 4:1 Product Size 6.0-12.0 mm Markets:
Automotive, Industrial
Standards:
Design for major Automotive OEM sealing specifications
Typical Applications:
Termination & protection of end and stub splices
-
Technical Data：
Test Items
Test Method
Test Requirements
Tensile strength
ASTM D 2671
10.4MPa min.
Tensile strength after aging at 158 ℃ for 168 hrs
ASTM D 2671
7.3MPa min.
Elongation at break
ASTM D 2671
200% min.
Elongation at break after aging at 158 ℃ for 168 hrs
ASTM D 2671
100% min.
Heat shock at 225 °C for 4 hrs
UL 224
No dropping & cracking of outer jacket
Low-temperature flexibility at -30 °Cfor 4 hrs
ASTM D 2671
No cracking
Volume resistivity
ASTM D 2671
1014Ω.cm min.
Flammability (Black only)
ISO 6722-1
Self-extinguishing within 30 sec.
Heat aging 125 °C for 3000 hrs followed by
immersion leak resistance
GMW 17136
5μA max.
-
Product Dimensions：
Normal size
As supplied
After recovered
D*
(min.)
A*
(±10%)
C
(Max.)
d*
(Max.)
w*
(Min.)
Jacket wall (Min.)
Adhesive Wall
(Nom.)
mm
mm
mm
mm
mm
mm
mm
HBK CAP-1
5.72
30,35,40,50
9.0
1.27
1.5
0.80
0.75
HBK CAP-2
7.44
30,35,40,50
10.0
1.65
1.8
0.95
0.90
HBK CAP-3
10.85
40,50
10.0
2.41
2.2
1.15
1.10
D* = Inner diameter as supplied
d* = Inner diameter after fully recovered
w* = Total wall thickness after fully recovered
A* = Total length as supplied
Related products