HRA-6X
Applications:
Ideal for applications to extremely different diameter cables connectors and components. The very high shrink ratio Provides closely fit to a wide variety of irregular profile connector and figurations.
Features:
Heavy Wall Tubing with Hot Melting Adhesive
Shrink Ratio: 6:1
|
Resistant to UV-radiation
|
High electrical insulation
|
Superior mechanical property
|
Minimum fully recovery temperature: 120℃
|
北京丝袜按摩
Test Items |
Test Method |
Test Requirements |
Tensile strength |
ASTM D 2671 |
12MPa min. |
Ultimate elongation |
ASTM D 2671 |
350% min. |
Tensile strength after |
ASTM D 2671 |
12MPa min. |
Aging at 150℃ for 168hrs |
Ultimate elongation after |
ASTM D 2671 |
300% min. |
Aging at 150℃for 168hrs |
Density |
ASTM D 792 |
1.0~1.1 g/cm3 |
Dielectric strength |
ASTM D 60243 |
12kV/mm(2mm) min. |
Volume resistivity |
ASTM D 2671 |
1012Ω.cm min. |
Low temperature flexibility |
ASTM D 2671 |
No cracking of outer jacket |
-40℃/ 4hrs |
Properties of hot melt adhesive |
|
|
Softening point |
ASTM E28 |
85+/-5℃ |
Peel strength(PE) |
ASTM D 2671 |
4N/cm min. |
Water absorption |
ISO 62 |
0.2% max. |
RoHS compliant.
Ordering Information:
Standard colors:
Black
Special colors:
N/A
Dimensions:
Size |
As supplied |
After recovered |
Standard length |
Size |
As supplied |
After recovered |
Standard length |
(mm) |
(mm) |
(mm) |
(m) |
(mm) |
(mm) |
(mm) |
(m ) |
|
D*(Min.) |
d*(Max.) |
w(Min.) |
|
|
D*(Min.) |
d*(Max.) |
w(Min.) |
|
19/3.2 |
19 |
3.2 |
3.2 |
1.0-1.22 |
69.8/11.7 |
69.8 |
11.7 |
4.7 |
1.0-1.22 |
33/5.5 |
33 |
5.5 |
3.4 |
1.0-1.22 |
88.9/17.1 |
88.9 |
17.1 |
4.7 |
1.0-1.22 |
44.4/7.4 |
44.4 |
7.4 |
3.6 |
1.0-1.22 |
119.4/22.9 |
119.4 |
22.9 |
4.7 |
1.0-1.22 |
50.8/8.3 |
50.8 |
8.3 |
4.7 |
1.0-1.22 |
235/40 |
235 |
40 |
4.7 |
1 |
D* = Inner diameter as supplied
d* = Inner diameter after fully recovered