HRTM
Applications：
It is designed for applications to seal and protect electrical splices, cable terminations and joints where electrical insulation and water proof are required. 3:1 shrink ratio allows it easily fit over irregular shape and large connectors.
Features：
Dual wall, hot melt adhesive lined by co-extrusion
|
Resistant to UV-radiation
|
|
High electrical insulation
|
|
Superior mechanical property
|
|
Minimum fully recovery temperature: 120℃
|
北京丝袜按摩
| Test Items |
Test Method |
Test Requirements |
| Tensile strength |
ASTM D 2671 |
12MPa min. |
| Ultimate elongation |
ASTM D 2671 |
350% min. |
| Tensile strength after |
ASTM D 2671 |
12MPa min. |
| Aging at 150℃ for 168hrs |
| Ultimate elongation after |
ASTM D 2671 |
300% min. |
| Aging at 150℃for 168hrs |
| Density |
ASTM D 792 |
1.0~1.1g/cm3 |
| Dielectric strength |
ASTM D 60243 |
12kV/mm(2mm) min. |
| Volume resistivity |
ASTM D 2671 |
1012Ω.cm min. |
| Low temperature flexibility |
ASTM D 2671 |
No cracking of outer jacket |
| -40℃/4hrs |
| Properties of hot melt adhesive |
|
|
| Softening point |
ASTM E28 |
105+/-5℃ |
| Peel strength(PE) |
ASTM D 2671 |
4N/cm min. |
| Water absorption |
ISO 62 |
0.2% max. |
RoHS compliant.
Ordering Information:
Standard colors:
Black
Special colors:
N/A
Dimensions:
| Size |
As supplied |
After recovered |
Standard length |
Size |
As supplied |
After recovered |
Standard length |
| (mm) |
(mm) |
(mm) |
(m) |
(mm) |
(mm) |
(mm) |
(m) |
| |
D*(Min.) |
d*(Max.) |
w(Min.) |
|
|
D*(Min.) |
d*(Max.) |
w(Min.) |
|
| 8/2 |
8 |
2 |
1.8 |
1.0-1.5 |
45/12 |
45 |
12 |
2.4 |
1.0-1.5 |
| 12/3 |
12 |
3 |
1.9 |
1.0-1.5 |
55/16 |
55 |
16 |
2.4 |
1.0-1.5 |
| 16/5 |
16 |
5 |
1.9 |
1.0-1.5 |
65/19 |
65 |
19 |
2.6 |
1.0-1.5 |
| 19/5 |
19 |
5 |
1.9 |
1.0-1.5 |
75/22 |
75 |
22 |
2.8 |
1.0-1.5 |
| 22/6 |
22 |
6 |
2.1 |
1.0-1.5 |
95/25 |
95 |
25 |
3.1 |
1.0-1.5 |
| 28/6 |
28 |
6 |
2.6 |
1.0-1.5 |
115/34 |
115 |
34 |
3.5 |
1.0-1.5 |
| 33/8 |
33 |
8 |
2.4 |
1.0-1.5 |
140/42 |
140 |
42 |
3.4 |
1.0-1.5 |
| 40/12 |
40 |
12 |
2.4 |
1.0-1.5 |
160/50 |
160 |
50 |
3.4 |
1.0-1.5 |
D* = Inner diameter as supplied
d* = Inner diameter after fully recovered