H-175K
Applications：
H-175K is semi-rigid, excellent flame retardant heat-shrinkable Polyvinylidene fluoride (PVDF) tube for applications requiring high temperature performance, outstanding abrasion and cut through resistance or superior chemical and solvent resistant properties.
Features：
|
Approval: UL, VW-1, File No.E249362
|
|
Meet: RoHS, SAE-AMS-DTL-23053/18
|
|
Operating temperature: -55℃ to + 175℃
|
|
Minimum fully recovery temperature: 175℃
|
北京丝袜按摩
| Test Items |
Test Method |
Test Requirements |
| Tensile strength |
ASTM D 2671 |
34.5MPa minimum |
| Ultimate elongation |
ASTM D 2671 |
150% minimum |
| Ultimate elongation after |
UL 224 |
50% minimum |
| Aging at 250℃ for 168hrs |
| Heat shock at 300℃ for 4hrs |
ASTM D 2671 |
No cracking & dripping |
| Dielectric strength |
ASTM D 2671 |
25kV/mm minimum |
| Volume resistance |
ASTM D 2671 |
1013Ω.cm minimum |
| Cold bend at -40℃ for 4hrs |
ASTM D 2671 |
No cracking |
| Flammability |
UL 224, VW-1 |
Pass |
UL, VW-1, File No.E249362
Meets: SAE-AMS-DTL-23053/18
Ordering Information:
Standard colors:
Black, Clear
Dimensions:
| Size |
As supplied |
After recovered |
| (Inch) |
(mm) |
(mm) |
| |
D*(Min.) |
d*(Max.) |
w*(Min.) |
| 3/64 |
1.2 |
0.6 |
0.20 |
| 1/16 |
1.6 |
0.8 |
0.20 |
| 3/32 |
2.4 |
1.2 |
0.23 |
| 1/8 |
3.2 |
1.6 |
0.23 |
| 3/16 |
4.8 |
2.4 |
0.23 |
| 1/4 |
6.4 |
3.2 |
0.23 |
| 3/8 |
9.5 |
4.8 |
0.28 |
| 1/2 |
12.7 |
6.4 |
0.32 |
| 3/4 |
19.1 |
9.5 |
0.36 |
| 1 |
25.4 |
12.7 |
0.41 |
D* = Inner diameter as supplied
d* = Inner diameter after fully recovered
w*= Wall thickness after fully recovered