HRSL
Applications：
Heat Shrink Cable Repair Sleeve
Features：
Quick and easy installation
Covered with thermo paint
Protection against mechanical stress
Sleeve and channel can be cut to suit shorter applications
For insulation on low voltage cable up to 1000V
Hot melt adhesive forms a durable, moisture resistant seal
Fit a wide range of cable sizes
北京丝袜按摩
| Properties |
Test Condition and Method |
Requirement |
| Bursting Strength |
Test Temp: 23 ±5℃ |
15MPa min. |
| Thermal Ageing |
168 hrs at 150℃±2℃ |
13.7MPa min |
| Bursting strength |
After free shrinkable |
14MPa min |
| Dielectric strength |
Electrode Surface |
Min 12kV/mm |
| Dia: 6mm |
| Wight: 50±2gms |
| Voltage steps: 2kV/20sec |
| Split Resistance |
Temp: 200±2℃ |
No split |
| Test time 23±3℃ |
Propagation |
| Carbon Content |
Heating rate: 20℃/min |
Min 2.6±0.25% |
| UV Res of Out/layer |
Gas flow rate: 300cc/min |
| Cold Crack Resistance |
Test temp ≤ -40℃ |
No cracking |
| Resistance to aggressive |
Test media: Fuel oil, petroleum |
Min 13.7MPa |
| media |
jelly |
| Bursting Strength |
Test temp: 70±2℃ |
| Environmental |
10% Igepal Co 630 |
No cracking |
| Stress cracking |
solution immersion |
| |
Time 30 days |
| |
Test Temp: 50±3℃ |
| Temp. indicating |
Completely conversion |
Completely conversion |
| paint conversion |
| Properties of adhesive |
|
|
| Adhesive Softening Point |
ASTM E28 |
90±10℃ |
| Peel Strength |
-PE at 23±2℃ |
Min 70N |
| -Pb at 23±2℃ |
| Shear Strength |
At 23±2℃ |
Min 100N |
| Copper Mirror test |
| Test time: 16hrs |
| Test temp: 60±℃ |
| Corrosive Effect |
ASTM D 1693 |
No effect |
RoHS compliant.
Dimensions:
| Size (mm) |
As supplied(mm) |
After recovered(mm) |
Standard Length |
| D*(mm) |
W*(Min.) |
d*(Max.) |
w*(Min.) |
L(mm) |
| 36/10 |
38 |
0.7 |
10 |
3.2 |
500, 750, 1000, 1500 |
| 55/13 |
57 |
0.7 |
13 |
3.2 |
500, 750, 1000, 1500 |
| 85/20 |
85 |
0.7 |
20 |
3.2 |
500, 750, 1000, 1500 |
| 108/27 |
110 |
0.7 |
27 |
3.2 |
500, 750, 1000, 1500 |
| 136/30 |
138 |
0.7 |
30 |
3.2 |
500, 750, 1000, 1500 |
| 180/50 |
183 |
0.7 |
50 |
3.2 |
500, 750, 1000, 1500 |
*NOTE: 1. D*= Diameter as supplied
2. d* = Diameter after recovered
3. W*= Thickness of sleeve as supplied
4. w*= Thickness of sleeve after fully recovered